In718
Cr
Nb
Mo
Ti
Cu
Fe
50.0-55.0
17.0-21.0
4.75-5.25
2.80-3.30
0.65-1.15
0.20-0.80
≤0.30
bal
Specifications and grades
of alloysAlloy #:
In718 nickel alloy dust
Particle Size:
15-45μm, 15-53μm, 53-120μm, 53-150μm
Morphology:
Spherical
Appearance:
Gray
Package:
Aluminum bag, Vacuum packing
Application:
3D Printing Nickel Alloy powder
Other Applications:
powder metallurgy(PM), injection molding(MIM), spray painting(SP) etc.
How 3D Printer Nickel Alloy In718 Powder is it made? Inconel718 is an alloy that can be difficult to work with in mechanical processing. This material must go through several steps. Warm-up It is important to clean the surface of your workpiece before, and during, the healing process. Inconel718 alloy can become brittle if it is exposed to sulfur, phosphorus and lead. Impure materials include water, fuel, paint, and even lubricating oil. You should not exceed 0.1% sulfur in fuel. As an example, the impurity level of natural and liquefied gases should be below 0.1%. The sulfur content for urban gas should also be lower than 0.25g/m3. Petroleum gas’ sulfur content should also be under 0.5%. Heating electric furnaces should possess a better temperature control capability. Furnace gas must either be neutral or weakly acidic, and it should not fluctuate in oxygen and reduceibility. Thermal processing Inconel718 is suitable for hot working temperatures between 1120 to 900. The cooling method that Inconel718 uses can be either water quenching (or other rapid cooling methods). To ensure maximum performance, the material should be hot worked and annealed within the appropriate time. When hot-processing, it should be heated to at least the temperature of its processing. The final temperature at which the material undergoes deformation should not fall below 20% in order to preserve its plasticity. Cold working Following solution treatment, cold work should be performed. Inconel718’s work hardening is higher than the austenitic steel. Therefore, the processing equipment must be modified accordingly. There should also be an intermediate process for annealing during coldworking. Heating treatment Materials will have different properties depending on how they are treated. Inconel718 alloy can achieve best mechanical properties with long-term aging due to its low diffusion rate. Polished This oxide is much more difficult than the stainless steel near the Inconel718 welding area. The oxide should be removed with a fine sanding machine. You will need to remove the oxide with either sandpaper or salt water before you can pickle in a mixture acid of hydrofluoric and nitric acids. Machining Inconel718 can be machined after it has been treated with solution. Also, the work hardening process should be considered. Inconel718, unlike other austenitic stainless-steel steels, can be cut with low speeds. Welding The precipitation-hardening type Inconel718 alloy is very suitable for welding and has no tendency to crack after welding. These materials have many major benefits, such as high strength and ease-of-processing. Inconel718 has been designed for use in arc welding, plasma welding, and other similar applications. It is recommended that the metal surface be completely clean and free of any oil or powder prior to welding. The bright metal must be polished no later than 25 mm after the weld. 3D Printing with Nickel Alloy IN718 – Powder This nickel alloy’s original material, Inconel in718, is used for additive manufacturing and 3D printing. In718 exhibits good fatigue resistance, tensile strength and fracture resistance. It can withstand creep up to 700°C at high temperatures and is very resistant to corrosion. Inconel In718 may also be heated treated. Inconel718 has a wide range of applications due to its extensive properties. These include liquid fuel rockets. Rings and casings. Sheet metal components for planes and land-based turbine engines. Cryogenic storage tanks. Fastening parts. It is extremely heat resistant, which makes it suitable for many high temperature applications such as gas turbines and aerospace. Additional applications are pumps and measuring devices in energy and process technologies. Condition of IN718 Pulver: IN718 Powder dispersion performance will be affected by damp reunion. IN718 Powder should be stored in vacuum packaging and in a cool dry place. Additionally, IN718 powder shouldn’t be exposed to extreme stress. Shipping and Packing of IN718 powder: There are many options for packing, which all depend on IN718’s powder amount. Powder packaging for IN718,100g, 500g and 1kg/bag. Maximum 25 kg/barrel. Or as required. Shipping powder to IN718 could take place by air or sea as soon after receipt of payment. Advanced material 15giorni. Global chemical supplier and manufacturer (15giorni), has over 12 years of experience providing high-quality chemicals. Send us an enquiry if you’re interested in high-quality In718 Powder. (brad@ihpa.net)Nickel Alloy INS718 Powder Properties
Nickel Alloy INS718 Powder Health & Safety Information
Inquiry us